Résumé
In this study, polymer compounds consisting in a recycled polyolefin matrix (high or low density polyethylene (HDPE or LDPE)) and ground tyre rubber (GTR) powder are developed. The major problem in this two phase systems is the very poor interfacial adhesion between thermoplastic matrix and rubber filler, which impairs the mechanical properties of the compound. Two treatments have been tested to improve the adhesion and so the mechanical performances: GTR powder was oxidized either by reaction with potassium permanganate aqueous solution (0-20%wt of KMnO_4) or by irradiation (gamma-irradiation: 0-100 kGy). Oxidized GTR powders were then introduced into a HDPE matrix containing Maleic Anhydride grafted HDPE as a compatibilizing agent. While no significant improvement of mechanical properties was observed for the irradiated GTR powder, the KMnO_4 treatment lead to improved Young’s modulus and yield stress, but the adhesion mechanism involved was not clearly identified. L’influence de l’incorporation de poudrettes de pneumatiques commerciales dans du polyéthylène (haute et basse densité) recyclé sur les propriétés mécaniques de mélanges PE/poudre a été étudiée. Les résultats des tests mettent en évidence la chute des performances en raison de l’absence d’adhésion matrice/particule. Deux traitements de comptabilisation ont donc été expérimentés. L’oxydation par irradiation gamma de la poudrette et son incorporation dans une matrice contenant une petite quantité de fonctions anhydride maléique n’a pas permis d’améliorer les propriétés mécaniques, bien que l’oxydation ait été effective. Un traitement par permanganate de potassium a donné au contraire des résultats intéressants, mais le mécanisme expliquant l’augmentation du module d’Young n’est pas encore élucidé.