Eye-safe midwavelength infrared InAs-GaSb strain layer superlattice p(+)-n(-)-n homojunction avalanche photodiodes (APDs) grown by solid source molecular beam epitaxy were fabricated and characterized. Maximum multiplication gain of 1800 was measured at -20 V at 77 K. Excess noise factors between 0.8 and 1.2 were measured up to gain of 300. Gain of 200 was measured at 120 K. Exponential nature of the gain as a function of reverse bias along with low excess noise factor at higher gain confirms single carrier electron-only impact ionization in the avalanche regime. Decrease in the multiplication gain at higher temperatures correlates with standard APD characteristics. (C) 2007 American Institute of Physics.