Abstract
The high failure strain of thermoplastic elastomers (TPEs) is a very desirable feature for rechargeable Li-ion batteries by improving the lifetime of high specific capacity anode materials that undergo mechanical fractures induced by large volume variations. In this work, poly(styrene-b-2-hydroxyethyl acrylate) called PS-b-PHEA was synthesized by a nitroxide meditated polymerization method. Owing to the use of a specific polystyrene macroinitiator (SG1), a suitable TPE copolymer with long hydroxyethyl acrylate blocks to ensure good mechanical properties is obtained for the first time. We show that the electrochemical properties of the PS-b-PHEA-coated SnSb anode are drastically improved by suppressing the crack formation at the surface of the electrode. Indeed, electrochemical characterization revealed that a high and stable gravimetric capacity over 100 cycles could be achieved. Moreover, excellent capacity reversibility was achieved when cycled at multiple C-rates and fast kinetics confirming the strong protection role of the polymer. The advanced chemical and mechanical properties of PS-b-PHEA open up promising perspectives to significantly improve the electrochemical performance of all electrodes that are known to suffer from large volume variations.