Résumé
Well-organized zirconia (ZrO 2) nanoparticles forming mesoporous materials have been successfully synthesized via a facile micelle-templating method using cetyltrimethylammonium bromide as a structure-directing template to control the nucleation/growth process and porosity. The systematic use of such a surfactant in combination with a microwave-assisted solvothermal (cyclohexane/water) reaction enabled the control of pore size in a narrow-size distribution range (3−17 nm). The effect of solvent mixture ratio on the porosity of the synthesized oxide was determined, and the controlled growth of zirconia nanoparticles was confirmed by means of powder X-ray diffraction, small-angle X-ray scattering, transmission electron microscopy, selected area electron diffraction, high-resolution transmission electron microscopy, X-ray photoelectron spectroscopy, thermogravimetric analysis, and Fourier transform infrared spectroscopy as well as N 2 physisorption isotherm analysis. Then, the as-prepared nanostructured zirconia oxides were treated with sulfuric acid to have sulfated samples. The catalytic performances of these mesoporous zirconia nanoparticles and their sulfated samples were tested for levulinic acid (LA) esterification by ethanol, with quantitative conversions of LA to ethyl levulinate after 8 h of reaction.