Résumé
Redox-Targeting Flow Batteries (RTFBs) are promising alternatives to classical vanadium-based batteries for large-scale and stationary energy storage. Typically, RTFBs are marked by higher energy densities thanks to the addition of solid boosters within aqueous systems, taking care to limit the use of critical raw materials. This work subsequently investigates the case of sodium titanium phosphate (NTP, NaTi2(PO4)3, 132.8 mAh/g) as a potential booster material for the negolyte side of aqueous RTFBs. Pure NTP and carbon-coated NTP (C-NTP) particles were synthesized and characterized by various techniques (X-ray, TEM, TGA, Raman). So-obtained NTP and C-NTP particles were found to be suitable for creating innovative porous composite boosters formed as centimeter-sized granules by dry processing. Porous composite granules with an open porosity of 65% and 50 wt % of immobilized NTP or C-NTP were successfully produced by an extrusion–dissolution process using a regular PVDF binder and PEO as a porogen agent. Subsequently, intensive electrochemical tests were performed using an innovative dual-mediator reaction system (Fe-Tiron and 2,7-AQDS). High NTP reactivity, with booster utilization rates of up to 84% of its theoretical capacity, can be achieved under flow conditions, with an increase in volumetric capacity by a factor of 1.5, from 4 Ah L–1 to 6 Ah L–1. The mediator concentration (10 – 100 mM) and the mediator/booster ratio (0.5 – 1) play key roles in NTP reactivity. The fundamental work also highlights the benefit of C-NTP, allowing higher reactivity at low mediator concentrations. The study consequently validates the potential of NTP as an interesting booster material in future RTFB applications, with its scalable extrusion–dissolution technique to create innovative porous booster granules.