Abstract
The core structures of dislocations in diopside have been calculated within the Peierls model, which assumes a planar core. 1/2 < 110 > dislocations can dissociate into two collinear partial dislocations. We show that [001] glide is very difficult in (010) and that a non-collinear dissociation of [001](100) (modelled within a Peierls-Nabarro-Galerkin approach) makes glide equally easy in (100) and {110}. A widely spread core structure corresponding to a low lattice friction has been found for [100](010) and [010](100) dislocations which is not supported by mechanical data and, together with TEM observations, suggests that another, probably non-planar core structure is possible for these dislocations.