Abstract
Micro hyper-Raman spectroscopy of PbMg1/3Nb2/3O3 (PMN) single crystal is performed at room temperature. The use of an optical microscope working in backscattering geometry significantly reduces the LO signal, highlighting thereby the weak contributions underneath. We clearly identify the highest frequency transverse optic mode (TO3) in addition to the previously observed soft TO-doublet at low frequency and TO2 at intermediate frequency. TO3 exhibits strong inhomogeneous broadening but perfectly fulfils the hyper-Raman cubic selection rules. The analysis shows that hyper-Raman spectroscopy is sensitive to all the vibrations of the average cubic Pm3m symmetry group of PMN, the three polar F1u- and the silent F2u-symmetry modes. All these vibrations can be identified in the Raman spectra alongside other vibrational bands likely arising from symmetry breaking in polar nanoregions.