Abstract
The radical co- and terpolymerization of perfluoro(4-methyl-3,6-dioxaoct- 7-ene) sulfonyl fluoride (PFSVE) with 1,1-difluoroethylene (or vinylidene fluoride, VDF or VF2), hexafluoropropene (HFP), chlorotrifluoroethylene (CTFE), and bromotrifluoroethylene (BrTFE) is presented. Although PFSVE could not homopolymerize under radical initiation, it could be copolymerized in solution under a radical initiator with VDF, while its copolymerizations with HFP or CTFE led to oligomers in low yields. The terpolymerizations of PFSVE with VDF and HFP, with VDF and CTFE, or with VDF and BrTFE also led to original fluorinated terpolymers bearing sulfonyl fluoride side-groups. The conditions of co- and terpolymerization were optimized in terms of the nature and the amount of the radical initiators, of the nature of solvents (fluorinated or nonhalogenated), and of the initial amounts of fluorinated comonomers. The different mol % contents of comonomers in the co- and terpolymers were assessed by 19F NMR spectroscopy. A wide range of co- and terpolymers containing mol % of PFSVE functional monomer ranging from 10 to 70% was produced. The kinetics of copolymerization of VDF with PFSVE enabled to assess the reactivity ratios of both comonomers: rVDF ¼ 0.57 6 0.15 and rPFSVE ¼ 0.07 6 0.04 at 120 8C. The thermal and physicochemical properties were also studied. Moreover, the glass transition temperatures (Tgs) of poly(VDF-co-PFSVE) copolymers containing different amounts of VDF and PFSVE were determined and the theoretical Tg of poly(PFSVE) homopolymer was deduced. Then, the hydrolysis of the SO2F into SO3H function was investigated and enabled the synthesis of fluorinated copolymers bearing sulfonic acid functions.