Abstract
The demand for high energy density Li‐ion batteries requires electrode materials with high capacity and long cycling stability. Silicon is among the most promising negative electrode materials due to its high theoretical capacity, abundant resources, and low working potential. However, its poor conductivity and significant volume expansion during cycling limit its practical application. To overcome these issues, this study develops a two‐step synthesis method for a nanostructured composite based on silicon as the active material. First, a crumbled Ti 3 C 2 T x (c‐Ti 3 C 2 T x ) structure formed through electrostatic interaction between a Ti 3 C 2 T x suspension and 1 M KOH. Then, an amorphous silicon layer is electrodeposited onto the c‐Ti 3 C 2 T x flakes in a room‐temperature ionic liquid, creating the Si/c‐Ti 3 C 2 T x composite for the negative electrode of Li‐ion batteries. The c‐Ti 3 C 2 T x structure enhances conductivity, provides mechanical stability to accommodate silicon's expansion, and offers nanostructured porosity for lithium‐ion diffusion. The composite material demonstrates exceptional cycling stability, achieving a capacity of 1300 mAh g −1 at C/5 with 91 % capacity retention after 100 cycles.