Abstract
Transition metal dichalcogenides have gained much attention due to their semiconducting properties, enabling a wealth of applications that integrate these 2D materials. Optical properties such as luminescence and nonlinear optical properties are of particular interest for photonic applications despite the small surface of the individual exfoliated flakes or the inherent difficulty to mechanically transfer flakes grown by CVD onto a given substrate. Herein, we investigate the Langmuir-Blodgett transfer of exfoliated MoS2 flakes deposited onto glass coverslips. Intercalation of Au and SiO2 nanoparticles between 2 layers of MoS2 was conducted using successive LB deposition, enabling the formation of heterostructures films with conductor and dielectric materials. The properties of these films were investigated using Raman spectroscopy and second harmonic generation (SHG) microscopy. The multilayers films are transferred on ∼ cm2 surface area with good coverage but with uncontrolled crystalline orientation of the MoS2 flakes. Raman enhancement of MoS2 was evidenced when Au nanoparticles are intercalated between two layers of MoS2. Polarized SHG microscopy shows a transition from quadrupolar response of the MoS2 flake driven by their D3h symmetry to a dipolar polarized response driven by the Au nanoparticles.