Abstract
The development of third generation Solid Oxide Fuel Cells (SOFC) with metallic mechanical supports presents several advantages over that of ceramic stacks by offering a lower cost and longer lifetime of the stacks. As a consequence, it is necessary to prepare metallic porous compacts that remain stable at the operating temperature of the SOFC (700–800 C) under reductive atmosphere. This paper presents an innovative process to elaborate iron, nickel and cobalt porous compacts. The process is based on the thermal decomposition of metal oxalate precursors with controlled morphology into metallic powders with coralline shape. Uniaxial compaction of such powders (without binder addition to the powders) under low uniaxial pressures (rising from 20 to 100 MPa) gave rise to green compacts with high porosity and good mechanical properties. After annealing at 800 C under H2 atmosphere, the compacts still present interconnected porosity high enough to allow sufficient gas flow to feed a SOFC single cell in hydrogen: the porosity rises from 25 to 50% for iron compacts, from 20 to 50% for cobalt compacts, and is higher than 40% for nickel compacts. Results from physicochemical characterization (XRD, SEM, gas permeation, Hg porosimetry) corroborated the process for SOFC application.