Résumé
Fe-containing SiBEA zeolites were prepared by a two-step postsynthesis method: creation of vacant T-sites by dealumination of tetraethylammonium BEA zeolite with nitric acid and then impregnation of the resulting SiBEA zeolite with an aqueous solution of Fe(NO
3)
3. X-ray diffraction shows that iron is incorporated in SiBEA at lattice sites. The presence of Fe in its oxidation state +3 and at isolated tetrahedral sites for low metal content, was demonstrated by diffuse reflectance UV–vis, EPR and Mössbauer spectroscopy. For high iron content, diffuse reflectance UV–vis and Mössbauer spectra revealed the additional presence of extra-lattice FeO
x
oligomers and superparamagnetic Fe-oxyhydroxide. Mössbauer spectroscopy identified superparamagnetic Fe-oxyhydroxide as the main phase when basic conditions are used for the preparation.