Résumé
An experimental work is presented that aimed at improving our understanding of the mechanical evolution of cracks under brittle creep conditions. Brittle creep may be an important slow deformation process in the Earth's crust. Synthetic glass samples have been used to observe and document brittle creep due to slow crack-propagation. A crack density of 0.05 was introduced in intact synthetic glass samples by thermal shock. Creep tests were performed at constant confining pressure (15 MPa) for water saturated conditions. Data were obtained by maintaining the differential-stress constant in steps of 24 h duration. A set of sensors allowed us to record strains and acoustic emissions during creep. The effect of temperature on creep was investigated from ambient temperature to 70 degrees C. The activation energy for crack growth was found to be 32 kJ/mol. In secondary creep, a large dilatancy was observed that did not occur in constant strain rate tests. This is correlated to acoustic emission activity associated with crack growth. As a consequence, slow crack growth has been evidenced in glass. Beyond secondary creep, failure in tertiary creep was found to be a progressive process. The data are interpreted through a previously developed micromechanical damage model that describes crack propagation. This model allows one to predict the secondary brittle creep phase and also to give an analytical expression for the time to rupture. Comparison between glass and crystalline rock indicates that the brittle creep behavior is probably controlled by the same process even if stress sensitivity for glass is lower than for rocks.