Résumé
A general method is proposed to produce oriented and highly crystalline conducting polymer layers. It combines the controlled orientation/crystallization of polymer films by high-temperature rubbing with a soft-doping method based on spin-coating a solution of dopants in an orthogonal solvent. Doping rubbed films of regioregular poly(3-alkylthiophene) s and poly(2,5-bis(3-dodecylthiophen- 2-yl) thieno[3,2-b] thiophene) with 2,3,5,6-tetrafluoro-7,7,8,8-tetracyanoquinodimethane (F(4)TCNQ) yields highly oriented conducting polymer films that display polarized UV-visible-near-infrared (NIR) absorption, anisotropy in charge transport, and thermoelectric properties. Transmission electron microscopy and polarized UV-vis-NIR spectroscopy help understand and clarify the structure of the films and the doping mechanism. F(4)TCNQ(-) anions are incorporated into the layers of side chains and orient with their long molecular axis perpendicular to the polymer chains. The ordering of dopant molecules depends closely on the length and packing of the alkyl side chains. Increasing the dopant concentration results in a continuous variation of unit cell parameters of the doped phase. The high orientation results in anisotropic charge conductivity (sigma) and thermoelectric properties that are both enhanced in the direction of the polymer chains (sigma = 22 +/- 5 S cm(-1) and S = 60 +/- 2 mu V K-1 ). The method of fabrication of such highly oriented conducting polymer films is versatile and is applicable to a large palette of semiconducting polymers.