Résumé
The aim of this thesis was to fabricate core / shell structures based on zinc oxide (ZnO) nanowires for photovoltaic applications mainly, and UV sensors as well. ZnO nanowire arrays of controlled size were grown using electrodeposition method (ECD). We also synthesized organized urchins based on ZnO nanowires by combining methods of surface nanostructuring (self-assembly of polystyrene spheres), atomic layer deposition (ALD) and electrodeposition of ZnO (ECD). Several approaches concerning the control of dimensions on these nanowires have been investigated. The diameter, density and morphology of these nanowires were adjusted either by modifying the diameters of spheres or by modulating the experimental parameters during deposition (ALD and / or ECD). Organized monolayers and multilayers of urchins based on ZnO nanowires ranging between 750 -1500 nm in length were obtained in a diameter range between 50-170 nm. The construction of dye solar cells (DSSC) was based on nanowire arrays and organized urchins based on ZnO nanowires coated with thin shells of titanium oxide (TiO2) obtained by atomic layer deposition (ALD). As proof of concept, solar conversion efficiencies of ~ 2% were achieved, bearing in mind that ZnO absorbs only in UV range. These materials have also been used for solar cells construction of type II based on organized urchin-like ZnO nanowires coated with copper oxide (Cu2O) layers of different thicknesses by electrodeposition of Cu2O. The effects of the morphology and the dimension of the organized nanowires and urchin-like ZnO nanowires on light scattering and electronic performance of the devices have been studied. UV sensors were tested using nanowires and urchin-like ZnO nanowires. A significant improvement in the performance and stability in UV detection was observed when using these ZnO nanostructures. This is due to the increase in active area offered by the ZnO nanowires and urchins compared to the performance obtained with ZnO thin films. Finally, a bioelectrode based on polyacrylonitrile nanofibers (PAN) coated with a layer of gold has been prepared for the electrochemical reduction of CO2 into useful biofuels. The PAN/gold electrode was prepared using a homemade synthesis method, based on electrospinning followed by gold sputtering. A significant improvement in the electrochemical activity and the stability of the bioelectrode was observed.