Abstract
Reaction wood produces very peculiar maturation stresses at the tree periphery i.e. compressive stress or very high tensile stress, for compression and tension wood respectively, as compared to moderately high tensile stress for normal wood. This means that both its mechanical state and its mechanical and physical properties differ from normal wood. Compression wood shows big differences from normal wood in conifers, for all physical and mechanical properties: higher density and axial crushing strength (MOR) but lower modulus of elasticity (MOE), far higher axial (longitudinal) shrinkage but lower radial and tangential shrinkage, sometimes even lower than the axial shrinkage. For tension wood things are less simple and can vary a lot from hardwood species to species. Globally there are no systematic differences in density and transverse shrinkage, MOE tends to be a little higher while MOR is slightly lower. However, axial shrinkage is much higher for tension wood with a gelatinous layer (G layer) than normal wood due to the specific gel like organization of cellulose microfibrils in the G layer. For tension wood without a G layer(which is rather frequent) axial shrinkage in the first drying operation is around two times higher than in normal wood mainly because of a kind of hygro-thermal release of locked in maturation stress. Overall the very high tensile stress and stored elastic energy in tension wood lead to problemsin wood processing (end splitting and board warping), which is far less the case for compression wood. But due to the large difference in properties relative to normal wood, compression wood occurrence is always a big problem for the in service behaviour of timber, which is seldom the case for tension wood.